Title: Substrate Effects on Electrical Parameters of Dirac Fermions in Graphene
Authors: Tıraş, Engin
Ardalı, Şükrü
Fırat, Hakan Asaf
Arslan, Engin
Özbay, Ekmel
Keywords: Graphene
Titanium dioxide
Silicon
Shubnikov-de Haas oscillations
In-plane effective mass
Publisher: Elsevier
Abstract: The substrate effects on the electronic transport properties of single-layer graphene on TiO2/Si substrate have been studied. The Hall mobility, sheet carrier density, and transport lifetime were obtained from the temperature-dependent Hall measurements, while the in-plane effective mass, quantum lifetime was obtained from the temperature-dependent variation of the Shubnikov de Haas (SdH) oscillations that were made at 1.8 to 45 K temperature range and up to the magnetic field of 11 T. The measurement results showed that in SLG/TiO2/ Si sample, there were 2.36 +/- 0.12x1016 m-3 amounts of 3D carriers coming from the substrate. In our previous studies, 3D carrier densities were measured as 6.07x1016 m-3 and zero for SLG/SiO2/Si and SLG/SiC sample, respectively. This result shows that the 3D carriers formed in the structure are significantly changed by a substrate. The scattering mechanisms were determined using the zt/zq ratio. The ratio values obtained as 3.66. This value obtained was compared with the values we found for SLG/SiC (zt/zq=1.36) sample and SLG/TiO2/Si (zt/zq=3.08) sample our previous study. The results show that small-angle scattering is dominant in SLG/SiC sample, but large-angle scattering is dominant in SLG/SiO2/Si and SLG/TiO2/Si samples. The charged impurity scattering is the dominant scattering mechanism in SLG/TiO2/Si and SLG/SiO2/Si samples, whereas in SLG/SiC samples, a short-range scattering mechanism such as lattice defects can be said to affect the electronic transport.
URI: https://doi.org/10.1016/j.mssp.2021.105936
https://hdl.handle.net/11147/11555
ISSN: 1369-8001
1873-4081
Appears in Collections:Physics / Fizik
Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection

Files in This Item:
File SizeFormat 
1-s2.0-S1369800121002833-main.pdf2.28 MBAdobe PDFView/Open
Show full item record



CORE Recommender

Page view(s)

37,634
checked on Mar 31, 2025

Download(s)

2
checked on Mar 31, 2025

Google ScholarTM

Check




Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.