Title: Effect of Heat Treating Metallic Constituents on the Properties of Cu2znsnse4 Thin Films Formed by a Two-Stage Process
Authors: Olgar, Mehmet Ali
Başol, B. M.
Atasoy, Y.
Tomakin, Murat
Aygün, Gülnur
Özyüzer, Lütfi
Bacaksız, Emin
Keywords: Kesterite
Sputtering
Thin film solar cells
Soft annealing
Crystalline quality
Thin films
Publisher: Elsevier Ltd.
Source: Olgar, M. A., Başol, B. M., Atasoy, Y., Tomakin, M., Aygün, G., Özyüzer, L., and Bacaksız, E. (2017). Effect of heat treating metallic constituents on the properties of Cu2ZnSnSe4 thin films formed by a two-stage process. Thin Solid Films, 624, 167-174. doi:10.1016/j.tsf.2017.01.037
Abstract: In this study Cu2ZnSnSe4 (CZTSe) thin films were grown by a two-stage process that involved sputter deposition of a Cu/Sn/Zn/Cu metallic stack, annealing the stack at various temperatures for 30 min, evaporation of a Se cap over the metallic stack thus forming a precursor layer, and subjecting the precursor layer to a final high temperature reaction step at 550 °C. Different samples were prepared with annealing temperatures of the metallic stacks ranging from 200 °C to 350 °C. The results showed that heat treatment of the metallic stacks did not cause much change in their morphology and elemental composition, however their phase content changed noticeably when the anneal temperature was raised to 250 °C. Specifically, while the metallic films were dominated by CuSn and Cu5Zn8 phases at low temperatures, the dominant phase shifted to Cu6Sn5 at the annealing temperature of 250 °C and higher. Also formation of a distinct Cu3Zn2 phase was observed upon annealing at temperatures at or above 250 °C. After reaction with Se, the CZTSe layer obtained from the metallic film, which was annealed at 250 °C was found to be the best n terms of its composition, crystalline quality and purity, although it contained a small amount of CuSe. The other layers were found to contain small amounts of other secondary phases such as SnSe, CuSe2, ZnSe and Cu2SnSe3. SEM micrographs showed denser structure for CZTSe layers grown from metallic films annealed at or above 250 °C. Optical band gap, resistivity and carrier concentration of the best quality CZTSe film were found to be about 0.87 eV, 2 Ω-cm and 4 × 1017 cm− 3, respectively.
URI: http://doi.org/10.1016/j.tsf.2017.01.037
http://hdl.handle.net/11147/6341
ISSN: 0040-6090
Appears in Collections:Physics / Fizik
Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection

Files in This Item:
File Description SizeFormat 
6341.pdfMakale2.55 MBAdobe PDFThumbnail
View/Open
Show full item record



CORE Recommender

SCOPUSTM   
Citations

23
checked on Dec 13, 2024

WEB OF SCIENCETM
Citations

22
checked on Nov 16, 2024

Page view(s)

8,880
checked on Dec 9, 2024

Download(s)

882
checked on Dec 9, 2024

Google ScholarTM

Check




Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.