Title: Growth and characterization of aluminum doped transparent and conductive zinc oxidethin flims
Authors: Selamet, Yusuf
Ataç, Derya
Issue Date: 2010
Publisher: Izmir Institute of Technology
Izmir Institute of Technology
Abstract: This thesis focuses on fabrication, characterization and understanding physical properties of transparent and conductive Al doped zinc oxide (ZnO) thin films. Films were deposited by magnetron sputtering technique, using separate ZnO and Al targets. SiO2 and glass (microscope slides) were used as substrates. Growths were performed at room temperature in Ar environment at a constant pressure of 3 mTorr. Films were characterized by atomic force microscope, x-ray diffractometer, scanning electron microscope, UV-vis spectroscophotometer and four point probe electrical measurements. Using transmission data, band gaps of the films and using four point probe measurements, resistivities of films were calculated. Firstly properties of pure ZnO films were studied. They were found to be highly transparent; however their resistivity was very high that we could not measure with our instrument. Therefore, ZnO films were uniformly doped with Al. It was seen that decreasing Al content was improving electrical and optical properties. Al concentration of the films was decreased firstly by decreasing deposition power of Al. After that, content was further decreased by depositing stacks of doped and undoped layers (modulation doping). Following that, modulation doped films were deposited with applying RF bias power to substrates. All films were annealed at 300oC for 1 hour in vacuum. The lowest resistivity obtained in this study was 1.68x10-3 .cm. Transmittance and band gap of the corresponding film were 80% and 4.1 eV respectively. The film was fabricated by modulation doping accompanied with substrate bias of 10 W, followed by annealing at 300oC in vacuum.
Description: Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2010
Includes bibliographical references (leaves: 76-81)
Text in English; Abstract: Turkish and English
xiii, 81 leaves
URI: http://hdl.handle.net/11147/3044
Appears in Collections:Master Degree / Yüksek Lisans Tezleri
Sürdürülebilir Yeşil Kampüs Koleksiyonu / Sustainable Green Campus Collection

Files in This Item:
File Description SizeFormat 
T000221.pdfMasterThesis4.44 MBAdobe PDFThumbnail
View/Open
Show full item record

CORE Recommender

Page view(s)

10
checked on Dec 8, 2021

Download(s)

28
checked on Dec 8, 2021

Google ScholarTM

Check


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.