Title: Metal matrisli kompozitlerin yüksek deformasyon hızlarında davranışları
Other Titles: High strain rate deformation behavior of metal matrix composites
Authors: Güden, Mustafa
Hall, Ian W.
Güden, Mustafa
Izmir Institute of Technology. Mechanical Engineering
Keywords: Aluminum Metal Matrix Composites
Split Hopkinson Pressure Bar
Issue Date: 1999
Publisher: TMMOB Metalurji ve Malzeme Mühendisleri Odası
Source: Güden, M. & Hall, I. W. (1999). Metal matrisli kompozitlerin yüksek deformasyon hızlarında davranışları. Metalurji , 119, 20-28.
Abstract: Süreksiz katkılarla kuvvetlendirilmiş Alüminyum Metal Matris Kompozit'lere düşük ve yüksek deformasyon hızlarında basma deneyleri uygulanmıştır. Düşük hızlarda (10'3/S) basma deneyleri instron makinasi ile yapılmıştır. Split Hopkinson Pressure Bar teknigi yüksek hızlarda (>100 Is) basma deneylerinde kullanılmıştır.Parçacık, whisker ve kısa fiberlerle kuvvetlendiriimiş farklı matris (alüminyum) alaşımlı kompozitler test edilmiştir. Kuvvetlendiricinin deformasyon hızına bağlı gerilmeye etkilerini araştırmak için kompozitlerin kuvvetlendirilmemiş matris alaşımlarıda benzer deformasyon hızlarında test edilmiştir. Kuvvetlendiricinin boyutu ve dağılımının, matris alaşımı ve uygulanan Isıl işlemin test edilen kompozitlerde deformasyon hızına bağlı gerilmeleri etkilediği bulunmuştur.
Discontinuous fiber reinforced Aluminum Metal Matrix Composites have been compression tested at quasi-static and high strain rates. Quasi-static (10·3/s) compression tests were conducted using an instron machine. Split Hopkinson Pressure Bar technique was used to test composites at strain rates higher than 100/s. Tested composites were particulate, whisker and short fiber reinforced and contained different aluminum matrix alloys. In order to investigate effect of reinforcement on the strain rate dependent flow stress, unreinforced matrix alloys of the composites were also tested at similar strain rate regimes. It was found that reinforcement size and orientation, matrix alloy type and heat treatment had affected strain rate dependent flow stress!iehaviorG~e the tested metal matrix composites.
URI: http://hdl.handle.net/11147/4348
Appears in Collections:Mechanical Engineering / Makina Mühendisliği
TR Dizin İndeksli Yayınlar / TR Dizin Indexed Publications Collection

Files in This Item:
File Description SizeFormat 
Metal Matrisli.pdfMakale1.5 MBAdobe PDFThumbnail
View/Open
Show full item record

CORE Recommender

Page view(s)

2
checked on Jul 26, 2021

Google ScholarTM

Check


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.