An aluminum metal matrix composite reinforced with continuous unidirectional α-Al2O3 fibers has been compression tested at quasi-static and dynamic strain rates. In the transverse direction, the composite showed increased ...

Metal matrix composites, (MMC’s) provide several important advantages over unreinforced metals and alloys. Among these, higher moduli and yield stresses and enhanced thermo-mechanical properties are normally considered ...

Since accurate, reproducible methods of testing polymer composites are not very well developed or standardized, this research forms part of a program to gain a better understanding of the mechanical properties and failure ...

Strain rate dependent compression behavior of a plain-weave S-2 glass fabric SC-15 epoxy (rubber toughened resin) composite plate, currently studied as the backing plate for composite armor applications, was determined in ...

The Split Hopkinson Pressure Bar (SHPB), or Kolsky Bar, is widely used for studying the dynamic mechanical properties of metals and other materials. A cylindrical specimen is sandwiched between the incident and transmitter ...

Compression behavior of 15–26 Vf% Saffil™ short-fiber reinforced Al-1.17wt.%Cu alloy metal matrix composites has been determined over a strain-rate range of approximately 10−4 to 2×103 s−1. The strain-rate sensitivity of ...

An epoxy matrix filled with nonwoven mats of porous polystyrene (PS) fibers processed by an electrospinning was compression tested at quasi-static (1 × 10–3 s–1) and high strain (315 s–1) rates. The electrospun PS fibers ...

The compressive mechanical response of an FP™ continuous fiber (35 vol.%) Mg composite has been determined in the transverse and longitudinal directions at quasi-static and high strain rates. It was found that the composite ...

Quasi-static (~10−3s−1) and high strain rate (>500 s−1) compression behavior of an S2-glass woven fabric/vinyl ester composite plate was determined in the in-plane and through-thickness directions. In both directions, ...

Quasi-static (1 × 10−3–1 × 10−2 s−1) and high strain rate (∼1000 s−1) compressive mechanical response and fracture/failure of a (±45) symmetric E-glass/polyester composite along three perpendicular directions were determined ...