Title: Preparation and characterization of calcium stearate powders and films prepared by precipitation and Langmuir-Blodgett techniques
Authors: Gönen, Mehmet
Öztürk, Serdar
Balköse, Devrim
Okur, Salih
Ülkü, Semra
Keywords: Langmuir Blodgett films
Calcium
Carboxylation
Precipitation process
Calcium stearate
Bidendate
Nano films
Publisher: American Chemical Society
Source: Gönen, M., Öztürk, S., Balköse, D., Okur, S., and Ülkü, S. (2010). Preparation and characterization of calcium stearate powders and films prepared by precipitation and Langmuir-Blodgett techniques. Industrial and Engineering Chemistry Research, 49(4), 1732-1736. doi:10.1021/ie901437d
Abstract: The preparation of calcium stearate (CaSt2) using precipitation and Langmuir-Blodgett techniques was investigated in this study. While sodium stearate and calcium chloride were used in the precipitation process, calcium stearate nanofilms were produced from stearic acid and calcium chloride in sodium borate buffer with the Langmuir-Blodgett technique. Fourier transform infrared (FTIR) spectroscopy indicated carboxylate bands at 1577 and 1543 cm-1 in equal intensity in the powder form, but the films had a higher intensity 1577 cm-1 band than the 1543 cm-1 band. This showed the calcium ions associated with the COO- ions in the monodendate and bidendate structures in powders, and it was mainly in the bidendate structure in films. While characteristic peaks of CaSt2 at 2θ values of 6.40° and 19.58° were obtained in the X-ray diffraction (XRD) pattern of the dried powdered product, no sharp peaks were present in the 13 layer CaSt2 film. From scanning electron microscopy (SEM) micrographs, it was seen that calcium stearate powder had lamellar structure and the average particle size was 600 nm. The AFM picture of the CaSt2 film indicated the surface was not smooth with a peak to valley distance of 6 nm. © 2010 American Chemical Society.
URI: http://doi.org/10.1021/ie901437d
http://hdl.handle.net/11147/5931
ISSN: 0888-5885
Appears in Collections:Chemical Engineering / Kimya Mühendisliği
Physics / Fizik
Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection

Files in This Item:
File Description SizeFormat 
5931.pdfMakale2.85 MBAdobe PDFThumbnail
View/Open
Show full item record



CORE Recommender

SCOPUSTM   
Citations

56
checked on Mar 22, 2024

WEB OF SCIENCETM
Citations

50
checked on Mar 27, 2024

Page view(s)

290
checked on Mar 25, 2024

Download(s)

890
checked on Mar 25, 2024

Google ScholarTM

Check




Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.